Product Description:
Grilamid L 20 L is a medium viscosity Polyamide 12 (PA12) extrusion type. It is UV and heat stabilized. Its main features are high surface quality, very good UV and heat resistance, high abrasion resistance, good chemical and oil resistance, low weight, and low density.
Applications:
Grilamid L 20 L has been especially developed for high speed extrusion of thin walled primary copper wire insulation and secondary fiber optic cable sheathing as a protection against termites and ants.
Typical data:
Grilamid L 20 L is a medium viscosity Polyamide 12 (PA12) extrusion type. It is UV and heat stabilized. Its main features are high surface quality, very good UV and heat resistance, high abrasion resistance, good chemical and oil resistance, low weight, and low density.
Applications:
Grilamid L 20 L has been especially developed for high speed extrusion of thin walled primary copper wire insulation and secondary fiber optic cable sheathing as a protection against termites and ants.
Typical data:
| PROPERTY | TEST METHOD | UNIT | TYPICAL VALUE |
|---|---|---|---|
| Density | ISO 1183 | g/cc | 1.01 |
| Water Absorption | ISO 62 | % | 1.5 |
| Moisture Absorption | ISO 62 | % | 0.700 |
| Linear Mold Shrinkage, Flow | ISO 294-4, 2577 | cm/cm | 0.0080 |
| Linear Mold Shrinkage, Transverse | ISO 294-4, 2577 | cm/cm | 0.0080 |
| Hardness, Shore D | conditioned, 15s; ISO 868 | 70 | |
| Tensile Strength at Break | dry; ISO 527-1/-2 | MPa | 50.0 |
| conditioned; ISO 527-1/-2 | MPa | 50.0 | |
| Tensile Strength, Yield | dry; ISO 527-1/-2 | MPa | 40.0 |
| dry; ISO 527-1/-2 | MPa | 45.0 | |
| Elongation at Break | conditioned; ISO 527-1/-2 | % | >= 50 |
| dry; ISO 527-1/-2 | % | >= 50 | |
| Elongation at Yield | dry; ISO 527-1/-2 | % | 5.0 |
| conditioned; ISO 527-1/-2 | % | 12 | |
| Tensile Modulus | conditioned; ISO 527-1/-2 | GPa | 1.10 |
| dry; ISO 527-1/-2 | GPa | 1.40 | |
| Charpy Impact Unnotched | dry; ISO 179/1eU | NB | |
| conditioned; ISO 179/1eU | NB | ||
| dry; ISO 179/1eU | NB @Temperature 30.0 °C |
||
| conditioned; ISO 179/1eU | NB @Temperature 30.0 °C |
||
| conditioned; ISO 179/1eA | J/cm² | 0.800 | |
| conditioned; ISO 179/1eU | 0.400 J/cm² @Temperature 30.0 °C |
||
| Volume Resistivity | conditioned; IEC 60093 | ohm-cm | 1.00e+13 |
| Surface Resistance | IEC 60093 | ohm | 1.00e+12 |
| Dielectric Strength | conditioned; IEC 60243-1 | kV/mm | 32.0 |
| Comparative Tracking Index | conditioned; IEC 60112 | V | 600 |
| CTE, linear, Parallel to Flow | ISO 11359-1/-2 | ISO 11359-1/-2 | 120 |
| CTE, linear, Transverse to Flow | ISO 11359-1/-2 | ISO 11359-1/-2 | 140 |
| Melting Point | 10°C/min; ISO 11357-1/-3 | °C | 178 |
| Maximum Service Temperature, Air | long term; EMS | °C | 80.0 - 110 |
| short term; EMS | °C | 150 | |
| Deflection Temperature at 0.46 MPa (66 psi) | ISO 75-1/-2 | °C | 130 |
| Deflection Temperature at 1.8 MPa (264 psi) | ISO 75-1/-2 | °C | 50 |
| Flammability, UL94 | IEC 60695-11-10 | HB |