| Molding shrinkage (parallel) | ISO 294-4 | % | 2 / * |
| Molding shrinkage (normal) | ISO 294-4 | % | 2 / * |
| Tensile modulus | ISO 527-1/-2 | MPa | 2900 / 1000 |
| Yield stress | ISO 527-1/-2 | MPa | 90 / 50 |
| Nominal strain at break | ISO 527-1/-2 | % | 25/ >50 |
| Flexural modulus | ISO 178 | MPa | 2600 / 900 |
| Charpy notched impact strength (+23°C) | ISO 179/1eA | kJ/m2 | 5 / 30 |
| Izod notched impact strength (23°C) | ISO 180/1A | kJ/m2 | 5 / 30 |
| Melting temperature (10°C/min) | ISO 11357-1/-3 | °C | 295 / * |
| Temp. of deflection under load (1.80 MPa) | ISO 75-1/-2 | °C | 190 / * |
| Coeff. of linear therm. expansion (parallel) | ISO 11359-1/-2 | E-4/°C | 0.8 / * |
| Coeff. of linear therm. expansion (normal) | ISO 11359-1/-2 | E-4/°C | 1 / * |
| Burning Behav. at 1.5 mm nom. thickn. | IEC 60695-11-10 | class | HB / * |
| Thickness tested | IEC 60695-11-10 | mm | 1.5/ * |
| UL recognition | -- | -- | UL/ * |
| Burning Behav. at thickness h | IEC 60695-11-10 | class | HB/ * |
| Thickness tested | IEC 60695-11-10 | mm | 3/ * |
| UL recognition | -- | -- | UL/ * |
| Thermal Index 5000 hrs | IEC 60216/ISO 527-1/-2 | °C | 152 |
| Volume resistivity | IEC 60093 | Ohm*m | 1E12 / 1E7 |
| Comparative tracking index | IEC 60112 | -- | 400 / 400 |
| Humidity absorption | Sim. to ISO 62 | % | 3.2 / * |
| Density | ISO 1183 | kg/m3 | 1250 / - |