| PROPERTY | TEST METHOD | UNIT | TYPICAL VALUE |
|---|---|---|---|
| Specific Gravity | ASTM D792 | g/cm3 | 1.14 |
| Molding Shrinkage-Flow | ASTM D 955 | % | 1.7 to 2.3 |
| Water Absorption (Equilibrium, 23 ºC, 60% RH | ASTM D 570 | % | 1.3 |
| Tensile Strength at Yield (23 ºC) | ASTM D 638 | MPa | 85 |
| Tensile Elongation at Yield (23 ºC)) | ASTM D 638 | % | 50 |
| Flexural Modulus (23 ºC) | ASTM D 790 | MPa | 3000 |
| Flexural Modulus (23 ºC) | ASTM D 790 | MPa | 115 |
| Notched Izod Impact (23 ºC) | ASTM D 256 | J/m | 50 |
| Rockwell Hardness (RScale) | ASTM D 785 | -- | 118 |
| Deflection Temperature Under Load) (0.45 MPa, nannealed) (1.8 MPa, Unannealed) | ASTM D 648 | ºC | 233 95 |
| Melting Temperature | -- | ºC | 260 |
| Flame Rating | UL94 | -- | V-2 |