| Melt Flow Index | ASTM D1238 | g/10min | 18 |
| Density | ASTM D792 | g/cm³ | 0.9 |
| Tensile Stress (Yield) | ASTM D638 | kgf/cm2 | 300 |
| Tensile Strain (Break) | ASTM D638 | % | >100 |
| Flexural Modulus | ASTM D790 | kgf/cm2 | 12,000 |
| Rockwell Hardness | ASTM D785 | R | 95 |
| Notched Izod Impact Strength (23℃) | ASTM D256 | kgf·cm/cm | 5.5 |
| Notched Izod Impact Strength (-10℃) | ASTM D256 | kgf·cm/cm | 3.0 |
| Heat Deflection Temperature (4.6kgf/cm2) | ASTM D648 | ℃/td> | 95 |
| Haze | ASTM D1003 | % | 20 |
| Melt Flow Index | ISO 1133 | g/10min | 18 |
| Density | ISO 1183 | g/cm3 | 0.9 |
| Tensile Stress (Yield) | ISO 527-1 | kgf/cm2 | 26 |
| Tensile Strain (Break) | ISO 527-1 | % | >100 |
| Flexural Modulus | ISO 178 | kgf/cm2 | >9.900 |
| Notched Izod Impact Strength (23℃) | ISO 180 | kgf·cm/cm | 5.0 |
| Notched Izod Impact Strength (-10℃) | ISO 180 | kgf·cm/cm | 2.5 |
| Heat Deflection Temperature (4.6kgf/cm2) | ISO 75-1 | ℃ | 85 |
| Haze | - | % | 20 |