| Density | ISO 1183 | g/cm3 | 0.924 |
| Melt Mass-Flow Rate (MFR)(190˚C/2.16kg) | ISO 1133 | g/10min | 4.0 |
| Tensile Modulus | ISO 527-2 | MPa | 260 |
| Tensile Stress (Yield) | ISO 527-2 | MPa | 11.0 |
| Coefficient of friction | ISO 8295 | - | <0.20 |
| Film thickness-tested | | µm | 50 |
| Film thickness – Recommended/Available | | Mil (15-40µ) | 0.6-1.6 |
| Tensile Strength MD : 2.0 mil (50µm), Blown Film TD: 2.0 mil (50 µm), Blown Film | ISO 527-3 | MPa MPa | 19.0 16.0 |
| Tensile Elongation MD: 2.0 mil (50µm), Blown Film TD: 2.0 mil (50 µm), Blown Film | ISO R 527-3 | % % | 300 600 |
| Dart Drop Impact mil (50 µm), Blown Film | ASTM D1709 | g | 100 |
| Vicat Softening Temperature | ISO 306/A50 | ˚C | 92.0 |
| Melting Temperature (DSC) | ISO 3146 | ˚C | 111 |
| Glass 20˚, 1.97 mil (50 µm), Blown Film 60˚ , 1.97 mil (50 µm), Blown Film | ASTM D2457 | | >50 >100 |
| Haze (1.97 mil (50 µm), Blown Film) | ASTM 1003 | % | < 9.0 |