| MFI(190°C /2.16Kg) | ASTM D 1238 | gr/10Min | 2.3 |
| MFI(190°C /21.6Kg) | ASTM D 1238 | gr/10Min | - |
| Density | ASTM D 1505 | gr/cm³ | 0.920 |
| Haze | ASTM D 1003 | % | 12 |
| Gloss(45°) | ASTM D 2457 | % | 30 |
| Anti Oxidant | | | √ |
| Anti Block | | | √ |
| Slip Agent | | | √ |
| Dart Drop Impact | ASTM D 709(A) | g | 90 |
| Tear Strength MD/TD | ASTM D 1922 | gr/25μm | 100/300 |
| Tensile Strength at yield MD/TD | ASTM D 882 | MPa | 10/11 |
| Tensile Strength at Break MD/TD | ASTM D 882 | MPa | 30/25 |
| Elongation at Break MD/TD | ASTM D 882 | % | 1000/1100 |
| Secant Modulus MD/TD | ASTM D 882 | MPa | 80/100 |
| Coefficient of friction | ASTM D1894 | - | 0.13 |
| Vicat Softening Temperature | ASTM D 1525 | °C | 100 |
| Melting Point | BPC | °C | 123 |