| Melt Flow Rate(MFR) (190ºC/5kg) (190ºC/21.6kg) | ISO 1133 | g/10min | 045 12 |
| Density | ISO 1183 | g/cm³ | 0.945 |
| MRS Classification | ISO/TR 9080 | MPa | 8 |
| Hydrostatic Strength (80ºC) | ISO 1167 /DIN 8075 | hr | 1000 |
| Hydrostatic Strength (80ºC) | ISO 1167 /DIN 8075 | hr | 1000
|
| Tensile Modulus (23ºC, v= 1mm/min, Secant) | ISO 527-1,2 | MPa | 850 |
| Tensile Stress at yield (23ºC,v=50mm/min) | ISO 527-1,2 | MPa | 22 |
| Tensile Stress at yield (23ºC,v=50mm/min) | ISO 527-1,2 | % | 8 |
| Charpy Notch Impact Strength (23ºC) | ISO 179 | Kj/m2 | 12 |
| Hardness Shore D (3 Sec) | ISO 868 | -- | 60 |
| Vicat Softening Temperature | ISO 306 | ºC | 67 |
| Melting Point | ISO 3146 | ºC | 136 |