| Mass density (23ºC) | ASTM D 1505 | g/cm3 | 0.959 |
| Melt Flow Rate (190ºC/2.16kg) | ASTM D 1238 | gr/10Min | 0.35 |
| Melt Flow Rate (190ºC/5kg) | ISO 1133 | g/10min | 1.2 |
| Melt Flow Rate (190ºC/21.6kg) | ASTM D 1238 | g/10min | 23 |
| Izod impact strength | ASTM D 256 | Kg.cm/cm | 25 min |
| Yellow index | ASTM D 1925 | - | -5 |
| Ash content | ASTM D 1063 | wt% | 0.06 max |
| Volatile matter | ASTM D 1960 | wt%a | 0.05 max |
| Tensile strength at break | ASTM D 638 | gr/cm2 | 290 min. |
| Elongation at break | ASTM D 638 | % | 900 min |
| Melting point | ASTM D 2117 | ºC | 130 |
| Vicat softening point | ASTM D 1525 | ºC | 126 |
| ESCR | ASTM D 1693 | hr. | 15 |