| Density (Base resin) | ISO 1183/ISO 1872-2B | kg/m3 | 949 |
| Density (Compound) | ISO 1183/ ISO 1872-2B | kg/m3 | 959 |
| Melt Flow Rate (190°C/2.16 kg) | ISO 1133 | g/10 min | <0.1 |
| Melt Flow Rate (190°C/5.0 kg) | ISO 1133 | g/10 min | 0.25 |
| Tensile Stress at Yield (50 mm/min) | ISO 524-2 | MPa | 25 |
| Tensile Strain at Break | ISO 524-2 | % | >600 |
| Tensile Modulus (1 mm/min) | ISO 527-2 | MPa | 1100 |
| Charpy Impact, notched (0°C) | ISO 179/1eA | kJ/m2 | 16 |
| Hardness, Shore D | ISO 868 | - | 60 |
| Carbon Black Dispersion | ISO 18553 | - | <3 |
| Carbon Black content | ASTM D 1603/ISO 6964 | % | >2 |
| Brittleness Temperature | ASTM D 746 | °C | <-70 |
| Resistance to Rapid Crack (Pc at 0°C, test pipe | ISO 13477 | bar | >10 |
| Propagation, S4 test 250mm SDR11) | - | | |
| Resistance to Slow Crack (9.2bar, 80oC) | ISO 13479/td> | h | >1000 |
| Growth | - | | |
| Thermal Stability (210°C) | EN 728/td> | min | >20 |
| ESCR (10% lgepal), F50 | ASTM D 1693-A/td> | min | >10000 |