| Property | Test method | Unit | value |
|---|---|---|---|
| MFR ( 230˚ C/ 2.16 Kg ) | ASTM D1238/L | gr/10 min | 4.5 |
| Tensile Modulus of Elasticity (1mm/min) | ASTM D638 | MPa | 1500 |
| Tensile Strength at Yield (50 mm/min) | ASTM D638 | MPa | 34 |
| Elongation at Yield(50 mm/min) | ASTM D638 | % | 9 |
| Notched Charpy Impact at 23˚ | ISO 179/ 1eA | KJ/m2 | 3.5 |
| Notched Charpy Impact at -30˚ | ISO 179/ 1eA | KJ/m2 | 1.5 |
| Vicat Softening Point, 10N | ASTM D1525 | °C | 154 |
| Ball indentation hardness | ISO 2039-1 | MPa | 74 |
| HDT ( 0.46 N/mm2 ) | ASTM D648 | °C | 85 |
| Melting Point , DSC | ASTM D3417 | °C | 163 |
| Density | ASTM D792 | gr/cm3 | 0.91 |