| Property | Test method | Unit | value |
|---|---|---|---|
| Melt flow rata(230ºC/2.16 kg) | ASTM D1238L | dg/min | 3.2 |
| Density | ASTM D1505 | g/cm3 | 0.9 |
| Flexural Modulus | ASTM D790 | N/mm2 | 1650 |
| Tensile Strength at Yield | ASTM D790 | N/mm2 | 36 |
| Elongation at Yield | ASTM D638 | % | 11 |
| Izod impact Strength (notched) at 23ºC | ASTM D256 | J/m | 50 |
| Rockwell Hardness | ASTM D785 | R scale | 105 |
| Vicat softening point | ASTM D1525 | ºC | 156 |
| H.D.T (0.46 N/mm2) | ASTM D648 | ºC | 114 |
| Haze | ASTM D1003 | % | 35 |
| Glass | ASTM D523 | % | 63 |
| Accelerated oven ageing in air (forced circulation) at 150 ºC | ASTM D3012 | Hours | 150 |