| Density | ISO 1183 | g/cm3 | 1.20 |
| Melt mass-flow rate, MFR(230 ºC, 2.16kg) | ISO 1133 | g/10min | 10 |
| Molding shrinkage-flow | ASTM D955 | % | 0.50 to 0.70 |
| Water Absorption (23°C, 24hr) | ISO 62 | % | 0.10 |
| Tensile Stress (Yield) | ISO 527-2 | MPa | 62.0 |
| Tensile Stress (Break) | ISO 527-2 | % | 50 |
| Flexural Modulus | ASTM D790 | MPa | 2400 |
| Notched izod impact (23°C) | ASTM D256 | J/m | 600 |
| Heat Deflection Temperature 1.8 MPa, Unannealed | ISO 75-2/A | °C | 131 |
| Heat Deflection Temperature 8 (1.8 MPa, Annealed) | ISO 75-2/Ae | °C | 136 |
| Vicat Softening Temperature | ISO 306/B50 | °C | 150 |
| Flame rating (3.2 mm) | UL94 | | V-2 |