| Specific Gravity | ASTM D792 | g/cm2 | 1.20 |
| Melt Mass-Flow Rate (MFR)(300 ºC/1.2 kg) | ASTM D 1238 | g/10min | 10 |
| Molding Shrinkage - Flow | ASTM D 955 | % | 0.50 to0.70 |
| Tensile Strength (Yield) | ASTM D 638 | MPa | 61.8 |
| Tensile Elongation( Break) | ASTM D 638 | % | 110 |
| Flexural Modulus | ASTM D790 | Mpa | 2350 |
| Notched Izod Impact (3.18 mm) | ASTM D 256 | J/m | 850 |
| Rockwell Harness (R-Scale) | ASTM D785 | - | 120 |
| Deflection Temperature Under Load 1.8 Mpa, Unannealed | ASTM D 648 | ºC | 130 |
| Vicat Softening Temperature | ASTM D 15252 | ºC | 150 |
| Transmittance | ASTM D1003 | % | 89.0 |
| Haze | ASTM D1003 | % | <0.80 |