| Specific Gravity | ASTM D792 | - | 1.20 |
| Water Absorption (24 hours at 23℃) | ASTM D570 | % | 0.15 |
| Melt Flow Rate (300℃, 1.2kg) | ASTM D1238 | g/10min | 10 |
| Tensile Strength at yield | ASTM D638 | Kgf/cm2 | 700 |
| Tensile Elongation at break | ASTM D638 | % | 120 |
| Flexural Strength at yield | ASTM D790 | Kgf/cm2 | 880 |
| Flexural Modulus | ASTM D790 | Kgf/cm2 | 20.000 |
| Izod Impact Strength, notched, 23℃ (1/8”) | ASTM D256 | Kgf cm/cm | 85 |
| Rockwell Hardness | ASTM D785 | R scale | |
| HDT, 18.6 ㎏ ℃ D648 125 f/㎠ | ASTM D648 | ˚C | 125 |
| Coefficient of Linear Thermal Expansion | ASTM D696 | mm/mm/ ˚C | |
| Volume Resistivity | ASTM D257 | Ω.cm | 5~7×10-5 |
| Dielectric Strength | ASTM D149 | kV/mm | 4×1016 |
| Dielectric Constant | ASTM D150 | - | 30 |
| Dissipation Factor | ASTM D150 | - | |
| ARC Resistance | ASTM D495 | sec | 120 |
| UL-94 Flammability (1/16” thickness) | UL 94 | - | V-2 |
| Mold Shrinkage (3mm thickness) | ASTM D955 | % | 0.5~0.7 |