| Resin Identification | ISO 1043 | | POM |
| Part Marking Code | ISO 11469 | | >POM< |
| Yield Stress | ISO 527 | MPa | 69 |
| Yield Strain | ISO 527 | % | 10 |
| Strain at Break | ISO 527 | % | 38 |
| Nominal Strain at Break | ISO 527 | % | 25 |
| Tensile Modulus | ISO 527 | MPa | 3100 |
| Flexural Modulusv | ISO 178 | MPa | 2900 |
| Notched Charpy Impact Strength | ISO 179/1eA | kJ/m2 | 7 |
| Deflection Temperature 1.80MPa | ISO 75-1/-2 | °C | 95 |
| Deflection Temperature 1.80MPa | ISO 11357-1/-3 | °C | 178 |
| Melt Mass-Flow Rate 190°C, 2.16kg | ISO 1133 | g/10 min | 15 |
| Density | ISO 1183 | kg/m3 | 1420 |
| Melt Temperature Range | | °C | 210-220 |
| Melt Temperature Optimum | | °C | 215 |
| Mold Temperature Range | | °C | 80-100 |
| Mold Temperature Optimum | | °C | 90 |
| Drying Time, Dehumidified Dryer | | h | 2-4 |
| Drying Temperature | | °C | 80 |
| Processing Moisture Content | | % | <0.2 |
| Hold Pressure Range | | MPa | 80-100 |