| Molding shrinkage, parallel | ISO 294-4,2577 | % | 1.9 |
| Molding shrinkage, normal | ISO 294-4,2577 | % | 1.6 |
| Tensile Modulus | ISO 527-1/-2 | MPa | 3000 |
| Charpy notched impact strength, +23ºC | ISO 179/1eA | kJ/m2 | 6.8 |
| Charpy notched impact strength, -30ºC | ISO 179/1eA | kJ/m2 | 5.5 |
| Melting temperature, 10 ºC/min | ISO 11357-1/-3 | ºC | 165 |
| Temp. of deflection under load, 1.80 MPa | ISO 75-1/-2 | ºC | 97 |
| Temp. of deflection under load, 0.45 MPa | ISO 75-1/-2 | ºC | 152 |
| Vicat softening temperature, 50 ºC/h 50N | ISO 306 | ºC | 161 |
| Coeff. Of liner therm. Expansion, parallel | ISO 11359-1/-2 | E-6/K | 100 |
| Coeff. Of liner therm. Expansion, normal | ISO 11359-1/-2 | E-6/K | 120 |
| Water absorption | Sim. To ISO 62 | % | 0.75 |
| Humidity absorption | Sim .to ISO 62 | % | 0.2 |
| Density | ISO 1183 | Kg/m3 | 1480 |